Dual-component modified epoxy, based on polysulphides and epoxy resin.
Field of application:
Elastomere for joint filling of industrial floors with max. width = 10 mm
Support:
Concrete
Type of joint:
100 % dry extract coating
M ode of application
Support preparation:
Roughing and accurate undusting of joint lips and bottom; laying of a joint bottom at a depth at least equal to half of the width of the joint.
Implementation: Mix the parts A + B, if necessary apply a sticker on the joint to be filled. 1 to 2 hours after filling, when the product starts to take, smooth with a brush slightly permeated with MIBK diluent.
Conditions of application:
On slab after drying of min. 28 days
Ambient temperature and support > 15° C
Hygrometry < 80 %
Report mix weight: solution 80.6 – hardener 19.4
DPU :
1 hour - 20° C
Operating time decreases when the temperature increases
Use : Joint width 10 mm and depth 5 mm: 0.7 kg/10 ml
C haracteristics
Flash point
> 50°C
Density
Part A
1,4 kg/l
Part B
1.0 kg/l
Mix density
1,25 kg/l
Dry Extract
100 %
Appearance
Slightly gloss
Hardeness
Shore A : 87 (norme AFNOR NFT 51109)
Shore D : 32,2
Elongation
41 % (standard AFNOR 51034)
Pressure
2.35 MPA (Standard AFNOR NFT 51034)
Tests conducted in 7 days with a temperature of 23°C and a relative humidity of 50 %
Chemical resistance – 3 weeks of immersion at 20° C
Hydrochloric and acetic acids 10 %
Resistant
Phosphoric and lactic acids 5 %
Resistant
Nitric acids 3%
Resistant
Bases : soda 10 %
Resistant / sodium hydroxide 5 %
Resistant
Diverse
Toluene
Resistant
Trichlo and acetone
Accident falls
Acceptable resistance
Trichlo and acetone
Continously
Swelling and destruction
Fuel
Fuel
Resistant
Bleach 1 %
Bleach 1 %
Resistant
Vegetable oil and milk
Bleach 1 %
Resistant
P ackaging
Kit 2.5 kg
Part A: 2.015 kg
Part B: 0.485 kg
C olorouring
As required per RAL colour chart
NOTA : Please contact our technical department in cases of grounds with significant slope (permissible slope to flow the joint: 1 %).
LIMITATION OF LIABILITY
The information contained in this leaflet is provided for guidance based on our lnowledge. It does not constitute a waiver of our terms and conditions of sale an shall in no event imply any waranty by us or render us liable with regard to the use of our products.
For each project, a study should be jointly conducted with us.